NPR-80 Series
Developable Photo Imageable Solder Mask
NPR-80 is alkaline developable photo imageable solder mask (2-component type) .
These grades have been applied for fine patterned circuit boards in a wide range of fields since 1997.
Meanwhile, we provide various products that have long-term electric reliability for the recent fine patterning and can contribute to the reduction of environmentally hazardous substances.
Electric reliability
[Test condition] 85deg.C, 85%RH, DC60V
[Test coupon] Upisel 25N which has 100um pitched line.
Properties
| Item | Representative value | Test condition |
|---|---|---|
| Photosensitivity | 9 〜 11 29 〜 32 |
21 Step tablet 41 Step tablet |
| Resolution | 45um / 45um | Line / Space, Thickness about 20um, Scattering light 500mJ/cm2 |
| Flexibility | > 1cycles > 2,500cycles |
25um PI film, Angle 180deg., Pressure 50N MIT folding endurance test R=2.0mm, 土 135deg. |
| Pencil hardness | 5H | JIS K 5600 |
| Adhesion | Class 0 | JIS K 5600 |
| Heat resistance to solder | > 2cycles | Pb free solder paste, Reflow peak temp. 260deg.C, 30sec. |
| HHBT | > 2,000hours | 85deg.C, 85%RH, DC60V, 100um Pitch (L/S=50um/50um) |
| HAST | > 200hours | 110deg.C, 85%RH, DC60V, 100um Pitch (L/S=50um/50um) |
| Resistance to electroless Ni/Au Plating | PASS | Ni 3um / Au 0.08um thickness |
| Resistance to electrolytic Ni/Au Plating | PASS | Ni 3um / Au 0.1um thickness |
| Resistance to acid | PASS | 10% HCl aq., 25deg.C, 30min. Dipping |
| Resistance to alkaline | PASS | 5% NaOH aq., 25deg.C, 30min. Dipping |
| Resistance to organic solvent | PASS | IPA, 25deg.C, 30min. Dipping |
Products
| Name | Color | Features | Halogen Free |
|---|---|---|---|
| ID43 ID43YR |
Green Yellow |
Good flexibility | non-compliant |
| ID55B | Blue | Good long-term electrical reliability, Excellent flexibility | < 300ppm |
| ID60 | Green | Good flexibility, Flame resistance | non-compliant |